Bonded metal and thermoplastic components

ABSTRACT

A method for bonding components is provided. The method includes preparing a surface of a metal component, applying a film adhesive to the prepared surface, forming a thermoplastic component using injection molding such that the film adhesive is positioned between the metal component and the thermoplastic component, and curing the film adhesive.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a divisional application and claims priority to U.S. patentapplication Ser. No. 14/287,935 filed May 27, 2014 for “METHODS FORBONDING METAL AND THERMOPLASTIC COMPONENTS”, which is herebyincorporated by reference in its entirety.

BACKGROUND

The field of the disclosure relates generally to bonding components,and, more particularly, to bonding metal and thermoplastic componentsusing a film adhesive.

At least some known assemblies (e.g., in the aircraft industry) includeparts that combine metal and thermoplastic components. To assemble suchparts, thermoplastic components may be formed with one or moremechanical features that facilitate coupling the thermoplasticcomponents to associated metal components. For example, a thermoplasticcomponent may be formed on and around a metal component using injectionmolding to mechanically interlock with the metal component. However,under stress, the thermoplastic component may break or pop off of themetal component. Accordingly, at least some known assemblies includemetal and thermoplastic components bonded to one another using anadhesive.

At least some existing bonding solutions employ secondary bonding. Thesesolutions have a number of drawbacks, including additional surfacepreparation steps in order to achieve robust and cohesive failure modes,which adds cost and equipment. Secondary joining operations may alsolead to longer flow times to manufacture parts. Moreover, secondarybonding operations may also limit integration possibilities for hybridthermoplastic-metal parts.

BRIEF DESCRIPTION

In one aspect a method for bonding components is provided. The methodincludes preparing a surface of a metal component, applying a filmadhesive to the prepared surface, forming a thermoplastic componentusing injection molding such that the film adhesive is positionedbetween the metal component and the thermoplastic component, and curingthe film adhesive.

In another aspect, a method for forming a fastener having a dielectriccap is provided. The method includes preparing a surface on a head ofthe fastener, applying a film adhesive to the prepared surface, formingthe dielectric cap using injection molding such that the film adhesiveis positioned between the fastener head and the dielectric cap, andcuring the film adhesive to bond the dielectric cap to the fastenerhead.

In yet another aspect a part is provided. The part includes a metalcomponent, a thermoplastic component, and a film adhesive positionedbetween the metal and thermoplastic components, the film adhesivebonding the metal component to the thermoplastic component, wherein thepart is fabricated by applying the film adhesive to a surface of themetal component, forming the thermoplastic component using injectionmolding, and curing the film adhesive after the injection molding.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow diagram of an exemplary aircraft production and servicemethodology.

FIG. 2 is a block diagram of an aircraft.

FIG. 3 is a schematic view of a simple part that may be included on theaircraft shown in FIG. 2.

FIG. 4 is a schematic view of a complex part that may be included on theaircraft shown in FIG. 2.

FIG. 5 is a flow diagram that may be used to form the parts shown inFIGS. 3 and 4.

DETAILED DESCRIPTION

The systems and methods described herein facilitate bonding metal andthermoplastic components. The methods include applying a film adhesiveto a metal component and forming the thermoplastic component on themetal component and film adhesive using injection molding.

Referring more particularly to the drawings, implementations of thedisclosure may be described in the context of an aircraft manufacturingand service method 100 as shown in FIG. 1 and an aircraft 102 as shownin FIG. 2. During pre-production, exemplary method 100 may includespecification and design 104 of aircraft 102 and material procurement106. During production, component and subassembly manufacturing 108 andsystem integration 110 of aircraft 102 takes place. Thereafter, aircraft102 may go through certification and delivery 112 in order to be placedin service 114. While in service by a customer, aircraft 102 isscheduled for routine maintenance and service 116 (which may alsoinclude modification, reconfiguration, refurbishment, and so on).

Each of the processes of method 100 may be performed or carried out by asystem integrator, a third party, and/or an operator (e.g., a customer).For the purposes of this description, a system integrator may includewithout limitation any number of aircraft manufacturers and major-systemsubcontractors; a third party may include without limitation any numberof venders, subcontractors, and suppliers; and an operator may be anairline, leasing company, military entity, service organization, and soon.

As shown in FIG. 2, aircraft 102 produced by exemplary method 100 mayinclude an airframe 118 with a plurality of systems 120 and an interior122. Examples of high-level systems 120 include one or more of apropulsion system 124, an electrical system 126, a hydraulic system 128,and an environmental system 130. Any number of other systems may beincluded. Although an aerospace example is shown, the principles of thedisclosure may be applied to other industries, such as the automotiveindustry.

Apparatuses and methods implemented herein may be employed during anyone or more of the stages of production and service method 100. Forexample, components or subassemblies corresponding to production process108 may be fabricated or manufactured in a manner similar to componentsor subassemblies produced while aircraft 102 is in service. Also, one ormore apparatus implementations, method implementations, or a combinationthereof may be utilized during production stages 108 and 110, forexample, by substantially expediting assembly of or reducing the cost ofaircraft 102. Similarly, one or more of apparatus implementations,method implementations, or a combination thereof may be utilized whilethe aircraft 102 is in service, for example and without limitation, tomaintenance and service 116.

FIG. 3 is a schematic diagram of a simple part 300 that includes a metalcomponent 302, an adhesive 304, and an injection molded thermoplasticcomponent 306. Adhesive 304 bonds metal component 302 to thermoplasticcomponent 306, as described in detail herein. Simple part 300 may beincluded, for example, on aircraft 102 (shown in FIG. 2).

As used herein, part 300 is referred to as a ‘simple’ part because asingle interface 308 of metal component 302 is bonded to a singleinterface 310 of thermoplastic component 306. In one exampleimplementation, metal component 302 is a fastener (e.g., a bolt, ascrew, and/or any other type of fastening device having a head and ashank) and thermoplastic component 306 is a dielectric cap coupled tothe head of fastener via adhesive 304. For example, metal component 302may be a titanium fastener having a diameter of 0.485 inches,thermoplastic component 306 may be an unfilled 450G polyetheretherketone(PEEK) cap, and the formed simple part 300 may be an integral dielectrictop (IDT) fastener. Alternatively, metal component 302 and thermoplasticcomponent 306 may be any components that may be bonded to one another asdescribed herein. For example, in some implementations, thermoplasticcomponent 306 is polyaryletherketone (PAEK, PEKK), polyphenylene sulfide(PPS), polyetherimide (PEI), polycarbonate (PC), polyarylsulfone (PPS,PPSU, PSU), or polyphthalamide (PPA).

FIG. 4 is a schematic diagram of a complex part 400 that includes ametal component 402, an adhesive 404, and an injection moldedthermoplastic component 406. Similar to simple part 300 (shown in FIG.3), adhesive 404 bonds metal component 402 to thermoplastic component406, as described in detail herein. Complex part 400 may be included,for example, on aircraft 102 (shown in FIG. 2).

As used herein, part 400 is referred to as a ‘complex’ part becausemultiple interfaces 408 of metal component 402 are bonded to multipleinterfaces 410 of thermoplastic component 406. Accordingly, as comparedto simple part 300, complex part 400 is relatively complex. Notably,metal component 402 and thermoplastic component 406 may be any elementsthat may be bonded to one another as described herein.

FIG. 5 is a flow diagram of an exemplary method 500 for forming a part,such as simple part 300 (shown in FIG. 3) or complex part 400 (shown inFIG. 4). Method 500 includes preparing 502 a surface, applying 504adhesive to the surface, B-staging 506 the adhesive (i.e., partiallypre-curing or setting the adhesive), performing 508 an injection moldingprocess, and curing 510 the adhesive after the injection moldingprocess. The steps of method 500 are described in detail below.

Method 500 begins by preparing 502 a surface on the metal component.That is, in some implementations, the surface to which the adhesive willultimately be applied may initially include a coating (e.g., analuminum-pigmented coating that acts as a dry lubricant) that wouldinterfere with performance of the adhesive. Accordingly, the surface maybe prepared 502, for example, by grit blasting the surface to remove anysuch coating. For example, the surface may be grit blasted with #180grit alumina. To further prepare 502 the surface, a sol-gel coating(e.g., Boegel EPII sol-gel) may be applied to the surface after the gritblasting. To finalize the preparation 502, the surface of the metalcomponent may be primed with a corrosion inhibiting modified epoxyprimer.

After preparation 502, an adhesive is applied 504 to the surface. Whenthe metal component is a fastener, the surface may be the head of thefastener, which may be relatively small (e.g., 0.5 square inches). Inthe exemplary implementation, the adhesive is a film adhesive, and morespecifically, an epoxy film adhesive. For example, the adhesive may beEA9696U (0.03 lb/ft²) from Henkel Corp. Using an adhesive film ensuresthat the profile of the adhesive is relatively uniform. In the exemplaryimplementation, the adhesive is a toughened epoxy adhesive that providesrelatively strong environmental durability and mechanical strength forstructural bonding applications. Further, the adhesive cures at 250°Fahrenheit (F) or lower and is selected for its ability to withstandshort-term exposure to the relatively high thermoplastic processingtemperatures and adhesive kinetics.

Alternatively, the adhesive may be any suitable adhesive that enablesmethod 500 to be performed as described herein. For example, in someimplementations, depending on the application, the adhesive may cure athigher temperatures. Further, in some implementations, the film adhesiveis a urethane or polyimide adhesive. Moreover, in some implementations,the adhesive may be a spray-on adhesive. In the exemplaryimplementation, the adhesive is relatively thin (e.g., 0.002 to 0.005inches thick) to facilitate reducing overflow and vent blocking of aninjection molding tool during the injection molding process. However,depending on the part to be formed, the adhesive may be thicker (e.g.,up to 0.010 inches thick) in some implementations.

B-staging 506 is performed on the adhesive to facilitate restraining theflow of the adhesive during the subsequent injection molding process.That is, B-staging 506 is an intermediate process performed in an oventhat prepares the adhesive for the subsequent bonding operation byadvancing the adhesive through a viscosity profile. Parameters forB-staging 506 are selected based on predetermined cure kinetics of theadhesive. For example, in some implementations, B-staging 506 isperformed for approximately 30 minutes at approximately 180° F. In otherimplementations, B-staging 506 is performed for approximately 30 minutesat approximately 210° F. Alternatively, B-staging 506 may be performedusing any suitable parameters that enable method 500 to be performed asdescribed herein. For example, B-staging 506 may be performed for aperiod from 5 minutes to 2 hours, at temperatures between 150° F. and250° F. In some implementations, B-staging 506 is not performed.

The metal component and adhesive may be stored (e.g., for 24 hours)after B-staging 506 and prior to performing 508 injection molding. AfterB-staging 506, the injection molding process is performed 508.Specifically, at least a portion of the metal component (with theapplied adhesive) is placed in an injection molding tool, and thethermoplastic component is formed on the metal component and adhesiveusing injection molding. During injection molding, the metal componentand adhesive are subject to relatively high temperatures (e.g.,approximately 690° F.) and pressures (e.g., 8,000 psi) for a relativelyshort time (e.g., a few seconds). In some implementations, injectionmolding is performed at up to 725° F. and up to 15,000 psi. However, theB-staging 506 reduces flow of the adhesive during the injection moldingby partially curing the adhesive.

The adhesive is cured 510 after the injection molding process isperformed 508. For some thermoplastics, such as PEEK, the performance ofthe thermoplastic component is improved when the material is amorphous.Accordingly, during curing 510, in the exemplary implementation,temperatures are kept below a glass transition temperature of thethermoplastic component (e.g., about 290° F.). For example, curing 510may be performed for approximately 90 minutes at approximately 250° F.with temperature ramps of 7° F./minute at approximately 25 psi.Alternatively, curing 510 may be performed using any suitable parametersthat enable method 500 to be performed as described herein. For example,curing 510 may be performed at temperatures between 150° F. and 270° F.and at pressures from 10 psi to 95 psi. Curing 510 is performed in aheated press in the exemplary implementation.

Method 500 forms a high strength bond between the metal component andthe thermoplastic component. For example, based upon experimentalresults, at 75° F., resultant bonds produce a tension strength between1400 psi and 1600 psi to separate a titanium fastener from athermoplastic cap when the fastener and cap were bonded using thesystems and methods described herein. In contrast, at least some knownbonding techniques may produce a tension strength of approximately 600psi to separate bonded metal and thermoplastic components. Furthermore,the bonding methods described herein are relatively robust andrepeatable.

The implementations described herein provide systems and methods forbonding metal and thermoplastic components. The methods include applyingan epoxy adhesive to a metal component, B-staging the adhesive, andforming the thermoplastic component on the metal component and adhesiveusing injection molding. Notably, B-staging the adhesive reduces flow ofthe adhesive during the injection molding process.

The implementations described herein provide improvements over at leastsome known bonding methods. As compared to at least some known bondingmethods, the bond formed between metal and thermoplastic componentsusing the methods described herein is a stronger bond. Further, becausethe methods described herein enable the adhesive to withstand injectionmolding processes, parts including metal and thermoplastic componentsmay be formed relatively quickly and easily.

This written description uses examples to disclose variousimplementations, which include the best mode, to enable any personskilled in the art to practice those implementations, including makingand using any devices or systems and performing any incorporatedmethods. The patentable scope is defined by the claims, and may includeother examples that occur to those skilled in the art. Such otherexamples are intended to be within the scope of the claims if they havestructural elements that do not differ from the literal language of theclaims, or if they include equivalent structural elements withinsubstantial differences from the literal language of the claims.

What is claimed is:
 1. A part comprising: an injection molding tool fora thermoplastic component, said injection molding tool defining a cavityfor forming the thermoplastic component; a metal component having aninterface surface, said metal component at least partially disposed insaid injection molding tool; and a film adhesive positioned andpartially cured on said interface surface of said metal component, saidfilm adhesive defining at least one boundary of the cavity of saidinjection molding tool.
 2. A part in accordance with claim 1, whereinsaid metal component comprises a titanium fastener.
 3. A part inaccordance with claim 1, wherein said injection molding tool isconfigured to form the thermoplastic component comprising apolyetheretherketone (PEEK) cap.
 4. A part in accordance with claim 1,wherein said film adhesive is an epoxy film adhesive.
 5. A part inaccordance with claim 1, wherein said film adhesive is one of apolyurethane film adhesive and a polyimide film adhesive.
 6. A part inaccordance with claim 1, wherein said injection molding tool isconfigured to form the thermoplastic component comprising a dielectriccap.
 7. A part in accordance with claim 1, wherein said metal componentcomprises one of a bolt and a screw.
 8. A part in accordance with claim1, wherein said metal component comprises only a single interfacesurface configured to be bonded to a single interface of thethermoplastic component.
 9. A part in accordance with claim 1, whereinsaid metal component comprises multiple interface surfaces configured tobe bonded to multiple interfaces of the thermoplastic component.
 10. Apart in accordance with claim 1, wherein said part is fabricated bypreparing the surface of said metal component prior to applying saidfilm adhesive to the surface of said metal component.
 11. A part inaccordance with claim 10, wherein preparing the surface of said metalcomponent comprises priming the surface of said metal component using acorrosion inhibiting modified epoxy primer.
 12. A part in accordancewith claim 1, wherein said film adhesive comprises a thickness in arange of approximately 0.001 inches to 0.010 inches.
 13. A part inaccordance with claim 1, wherein said film adhesive comprises athickness in a range of approximately 0.002 inches to 0.005 inches. 14.A part in accordance with claim 1, wherein said adhesive film isconfigured to cure at no more than 250 degrees Fahrenheit.
 15. A partcomprising: a metal component comprising a titanium fastener; athermoplastic component; and a film adhesive positioned between saidmetal and thermoplastic components, said film adhesive bonding saidmetal component to said thermoplastic component, wherein said part isfabricated by applying said film adhesive to a surface of said metalcomponent, forming said thermoplastic component using injection molding,and curing said film adhesive after the injection molding.
 16. A part inaccordance with claim 15, wherein said thermoplastic component comprisesa polyetheretherketone (PEEK) cap.
 17. A part in accordance with claim15, wherein said film adhesive is an epoxy film adhesive.
 18. A part inaccordance with claim 15, wherein said film adhesive is one of apolyurethane film adhesive and a polyimide film adhesive.
 19. A part inaccordance with claim 15, wherein said thermoplastic component comprisesa dielectric cap.
 20. A part in accordance with claim 15, wherein saidmetal component comprises one of a bolt and a screw.